Production of Bio Charcoal Briquettes Made from Coal and Palm Fronds
Main Article Content
Sandi Asmara
Winda Rahmawati
Tamrin
Ipang Setiawan
Biomass from oil palm fronds has not been effectively utilized in Central Lampung, there is a need for alternative processing of palm oil fronds into more useful materials. One method of processing palm fronds is to create bio charcoal briquettes, which are used as an alternative fuel. The purpose of this research was to see how palm fronds and particle size of palm oil fronds affected the properties of bio charcoal briquettes. The factorial completely randomized design (CRD) was used in the research with one factor, namely the particle size of the oil palm fronds passing through the sieve with one treatment, namely 20 mesh. To produce 25 experimental units, the study used five treatments with five replications. The obtained material was then tested for LSD. The results revealed that palm fronds had no impact on briquette density, moisture content, compressive strength, shatter resistance index, or rate of burning. The particle size of palm leaves going through the 20 mesh sieve affects density, compressive strength, shatter resistance index, and burning rate significantly. The findings revealed the following features of bio charcoal briquettes: The moisture content is 5.17-6.89%, the heating value is 4372.42 - 5074.50 cal/g a density of 0.568-0.674 g/cm3, a compressive strength of 3.85 - 4.58 kg/cm2, a shatter resistance index of 12.58-17.19%, a burning rate of 1.40-1.47 gram/minute, and a bottom temperature of 287°C. (for 60 minutes and a mass of 200 grams).
Almu. A. M., Syahrul, & Yesung A. P. (2015). Analisa Nilai Kalor dan Laju Pembakaran Pada Briket Campuran Biji Nyamplung (Calophyllm Inophyllum) dan Abu Sekam Padi. Dinamika Teknik Mesin, 4(2), 117-124.
Badan Pusat Statistik. (2015). Statistik kelapa sawit di indonesia. Badan Pusat Statistik Republik Indonesia. http://www.bps.go.id/ (diakses 29 Maret 2019).
Caroko, N., Wahyudi, W., & Kurniawan, A. (2015). Analisa Karakteristik Pembakaran Briket Limbah Industri Kelapa Sawit Dengan Variasi Perekat dan Temperatur Dinding Tungku 300° C Menggunakan Metode Heat Flux Constant (HFC)
Damanhuri, E. (2010). Perhitungan Nilai Kalor Berdasarkan Komposisi dan Karakteristik Sampah Perkotaan di Indonesia dalam Konsep Waste to Energy. Jurnal Teknik Lingkungan, 16(2), 103-114.
Devendra, C. 1990. Roughage Resources for Feeding in The Asean Region, The First Asean Workshop on Technology of Animal Feed Production Utility Food Waste Material. Malaysia.
Ginting, S. P., & Elisabeth, J. 1997. Teknologi pakan berbahan dasar hasil sampingan perkebunan kelapa sawit. Prosiding Lokakarya Nasional: Sistem Integrasi Kelapa Sawit. 129-136.
Iriany., Firman, A. S. S., &Meliza. (2017). Pengaruh Perbandingan Tempurung Kelapa dan Eceng Gondok Serta Variasi Ukuran Partikel Terhadap Karakteristik Briket. Jurnal Teknik Kimia, 5(3), 56-63.
Jamilatun, S. (2008). Sifat-Sifat Penyalaan Dan Pembakaran Briket Biomassa, Briket Batubara dan Arang Kayu. Jurnal Rekayasa Proses, 2(2), 31-37.
Johannes, H. (1991). Menghemat Kayu Bakar dan Arang Kayu untuk Memasak di Pedesaan dengan Briket Arang. Laporan Karya Ilmiah Fakultas Teknik Universitas Gajah Mada.Yogyakarta : Gajah Mada University
Lubis, A. U. (1992). Kelapa Sawit (Elaeis guineensis. Jacq.) di Indonesia. Pusat Penelitian Perkebunan Marihat-Bandar Kuala. Sumatera Utara.
Prijono, A. (1992). Pengertian Batu Bara, dikutip dari ptba.co.id/en/Knowledge/index/pengertian-batubara. Tanggal 12 januari 2019
Purnomo, R. A., Haisen, H., & Inka, R. P. (2014). PemanfaatanLimbahBiomassa untuk Briket SebagaiEnergiAlternatif. Prosiding Seminar Agroindustri dan Lokakarya Nasional FKPT-TPI Program Studi TIP-UTM, 2(3), 56-67.
Rio, C. A. (2015). Rakteristik Briket Arang dari Tempurung Kelapa (Cocos NuciferaL) dengan Penambahan Bakau (RhizhophoraSpp) dan Laban (VitexPubescens). Skripsi. Institut Pertanian Bogor. Bogor.
Setiowati, R. & Triono, M. (2014). PengaruhVariasiTekananPengepresandan KomposisiBahanTerhadapSifatFisisBriketArang. Jurnal Neutrino, 7(1),23-31
Sudiro. S. (2014). Pengaruh Komposisi dan Ukuran Serbuk Briket yang Terbuat dari Batubara dan Jerami Padi Terhadap Karakteristik Pembakaran. Jurnal Sainstech Politeknik Indonusa Surakarta, 1(2), 1-20
Syamsiro, M. & Saptoadi, H. (2005). Pembakaran Briket Biomassa Cangkang Kakao Pengaruh Temperatur Udara Preheat. Seminar Nasional Teknologi. Universitas Gadjah Mada. Yogyakarta.
Tamrin. (2007). Lama Penyalaan dan Pematian Bara Api Terhadap Jumlah Massa Briket Batubara didalam Tungku. Seminar Nasional Sains dan Teknologi: Peran Strategis Sains dan Teknologi dalam Upaya Peningkatan Daya Saing Bangsa. Universitas Lampung. Lampung.
Tamrin. (2010). Pengembangan Tungku Briket Batubara Skala Rumah Tangga. Agritech, 30(4), 250-255.
Tamrin. (2010). Simulasi Perubahan Suhu dalam Ruangan Pembakaran Tertutup Saat Pematian Bara Api Briket Batubara. Prosiding Seminar Nasional Sains dan Teknologi III: Peran Strategi Sains dan Teknologi dalam Mencapai Kemandirian Bangsa. Universitas Lampung. Bandar Lampung.
Tamrin. (2011). Sifat Pembakaran Campuran Briket Batubara dengan Lima Jenis Biomassa. Prosiding Seminar Nasional dan Rapat Tahunan Dekan: Bidang Ilmu-Ilmu Pertanian BKS-PTN Wilayah Barat, 2. Universitas Lampung. Bandar Lampung.
Triono, A. (2007). Karakteristik Briket Arang dari Campuran Serbuk Gergajian Kayu Afrika (Measopsis eminii Engl) dan Sergon ( paraserianthes falcataria L. Nielsen) dengan Penambahan Tempurung Kelapa (Cocoa nurifera L.). Fakultas Kehutanan. Bogor: ITB.
Sandi Asmara , University of Lampung
Department Agriculture Engineering, Faculty of Agriculture, University of Lampung, Indonesia
Winda Rahmawati , University of Lampung
Department Agriculture Engineering, Faculty of Agriculture, University of Lampung, Indonesia
Tamrin , University of Lampung
Department Agriculture Engineering, Faculty of Agriculture, University of Lampung, Indonesia
Ipang Setiawan , University of Lampung
Department Agriculture Engineering, Faculty of Agriculture, University of Lampung, Indonesia